Effect of immediate dentin sealing and temporary cement removal on bond strength of resin cements to dentin / Efeito do selamento dentinário imediato e da remoção do cimento provisório na resistência de união de cimentos resinosos à dentina

Objective: To evaluate the influence of immediate dentin sealing (IDS) and mechanical methods for removing the temporary cement on the bond strength between dentin and resin cements. Material and Methods: Bovine incisors were ground until dentin exposure and divided according to two factors: "dentin surface treatment"' - cleaning with manual dental excavator (DE), with Robinson bristle brush and pumice paste (PP) or IDS application with Single Bond 2 (IDS/SB+PP) or Single Bond Universal (IDS/SBU+PP) plus cleaning with PP; and "resin cement" - Self-adhesive (RelyX U200) or conventional cement with self-etching adhesive (Multilink Automix). Simulating provisional restoration, acrylic resin plates were cemented onto the dentin surface (with or without IDS) with a non-eugenol temporary cement, and stored in distilled water (37 ºC; 7 days). The acrylic plates were removed, the dentin surface was cleaned (PP or DE), and starch tubes were positioned on the dentin where the resin cements were applied. After 24 h, the specimens were submitted to a microshear test (wire-loop method). Results: Two-way analysis of variance showed statistically significant influence of dentine surface treatments (p< 0.001) and resin cement (p= 0.001) in the bond strength values. The IDS/SBU+PP/U200 (7.24 MPa) and IDS/SBU+PP/MULTI (6.40 MPa) groups presented higher values when compared to cleaning with DE (DE/U200= 4.60 MPa; DE/MULTI= 1.45 MPa) and PP (PP/U200= 3.74 MPa; PP/MULTI= 3.14 MPa). Statistical difference was also found between the cements when dental excavator treatment was used (RelyX U200 ˃ Multilink Automix). The IDS/SBU+PP protocol presented a higher percentage of cohesive failures. The micrographs showed differences in dentin surface characteristics among the groups. Conclusion: Immediate dentin sealing increased the bond strength of the resin cements to dentin compared to mechanical cleaning only, regardless the resin cement. (AU)

Objetivo: Avaliar a influência do selamento dentinário imediato (IDS) e dos métodos mecânicos de remoção do cimento provisório na resistência de união entre dentina e cimentos resinosos. Materiais e Métodos: Incisivos bovinos foram desgastados até a exposição da dentina e divididos de acordo com dois fatores: "tratamento da superfície dentinária" - limpeza com cureta dentária manual (DE), com escova de cerdas Robinson e pasta de pedra-pomes (PP) ou aplicação de IDS com Single Bond 2 (IDS/SB +PP) ou Single Bond Universal (IDS/SBU+PP) mais limpeza com PP; e "cimento resinoso" - autoadesivo (RelyX U200) ou cimento convencional com adesivo autocondicionante (Multilink Automix). Simulando a restauração provisória, placas de resina acrílica foram cimentadas na superfície dentinária (com ou sem IDS) com um cimento provisório sem eugenol e armazenadas em água destilada (37 ºC; 7 dias). As placas de acrílico foram removidas, a superfície dentinária foi limpa (PP ou DE) e tubos de amido foram posicionados na dentina onde os cimentos resinosos foram aplicados. Após 24 h, os corpos-de-prova foram submetidos ao ensaio de microcisalhamento (método wire-loop). Resultados: A análise de variância de dois fatores mostrou influência estatisticamente significativa dos tratamentos de superfície dentinária (p< 0,001) e cimento resinoso (p= 0,001) nos valores de resistência de união. Os grupos IDS/SBU+PP/U200 (7,24 MPa) e IDS/SBU+PP/MULTI (6,40 MPa) apresentaram valores maiores quando comparados à limpeza com DE (DE/U200= 4,60 MPa; DE/MULTI= 1,45 MPa) e PP (PP/U200= 3,74 MPa; PP/MULTI= 3,14 MPa). Uma diferença estatística também foi encontrada entre os cimentos quando o tratamento com cureta dentária foi usado (RelyX U200 ˃ Multilink Automix). O protocolo IDS/SBU+PP apresentou maior percentual de falhas coesivas. As micrografias mostraram diferenças nas características da superfície dentinária entre os grupos. Conclusão: O selamento dentinário imediato aumentou a resistência de união dos cimentos resinosos à dentina em comparação com a limpeza mecânica apenas, independentemente do cimento resinoso.(AU)

The influence of roughness on the resistance to impact of different CAD/CAM dental ceramics

Abstract This study aimed to investigate the effect of surface roughness (polished vs. CAD/CAM milling simulation) on impact strength of five dental ceramics for manufacturing CAD/CAM monolithic restorations. Specimens of five ceramics (FC- feldspathic glass-ceramic; PICN- polymer-infiltrated ceramic-network; ZLS- zirconia-reinforced lithium silicate glass-ceramic; LD- lithium disilicate glass-ceramic; YZ- yttria-stabilized tetragonal zirconia polycrystal ceramic) to be tested under impact (15×10×2mm3; n= 15) were divided into two groups, according to surface treatment: polishing (pol) and grinding (gri) as CAD/CAM milling simulation. Impact strength was tested using the Dynstat method. Roughness, topographic, fractographic and finite element analyses were performed. The impact strength data were analyzed by Weibull, and Pearson correlation was used to correlate roughness and impact strength data. The CAD/CAM milling simulation led to significantly (p<0.05) greater roughness (Ra and Rz) and statistically reduced the impact strength for PICN (polPICN= 4.59 to griPICN= 1.09; ±76% decrease), for LD (polLD= 17.69 to griLD= 10.09; ±43% decrease) and for YZ (polYZ= 74.99 to griYZ= 20.67; ±72% decrease) ceramics; and also promoted a more irregular topography with scratches and grooves. Fractographic and FEA analyses depicted the origin of failure at the higher stress concentration side during the impact test, where the pendulum impacted. The CAD/CAM milling simulation significantly decreased the impact strength of the evaluated ceramic materials.

Resumo Este estudo teve como objetivo investigar o efeito da rugosidade da superfície (polido vs. simulação da usinagem em CAD/CAM) na resistência ao impacto de cinco cerâmicas odontológicas indicadas na fabricação de restaurações monolíticas em CAD/CAM. Espécimes de cinco cerâmicas (FC- vitrocerâmica feldspática; PICN- rede de cerâmica infiltrada com polímero; ZLS- vitrocerâmica de silicato de lítio reforçada com zircônia; LD- vitrocerâmica de dissilicato de lítio; YZ- cerâmica policristalina de zircônia tetragonal estabilizada com ítria), a serem testados sob impacto (15 × 10 × 2mm3; n= 15), foram divididos em dois grupos, de acordo com o tratamento superficial: polimento (pol) e desgaste (gri), usado como simulação da usinagem em CAD/CAM. A resistência ao impacto foi testada usando o método Dynstat. Foram realizadas as análises de rugosidade, topografia, fractografia e análise de elementos finitos. Os dados de resistência ao impacto foram analisados pela análise de Weibull, e a correlação de Pearson foi usada para correlacionar os dados de rugosidade e resistência ao impacto. A simulação da usinagem em CAD/CAM levou a uma rugosidade (Ra e Rz) significativamente maior (p < 0,05) para todas as cerâmicas, e reduziu estatisticamente a resistência ao impacto para as cerâmicas PICN (polPICN = 4,59 para griPICN = 1,09; redução de ± 76%), LD (polLD = 17,69 para griLD = 10,09; ± 43% de redução) e YZ (polYZ = 74,99 para griYZ = 20,67; ± 72% de redução); e também promoveu uma topografia mais irregular apresentando riscos e sulcos acentuados. As análises de fractografia e de elementos finitos mostraram a origem da falha no lado de maior concentração de tensão durante o teste de impacto, onde o pêndulo impactou o espécime. A simulação da usinagem em CAD/CAM reduziu significativamente a resistência ao impacto dos materiais cerâmicos avaliados.

Influence of testing environment on static fatigue behavior of a glass and a polycrystalline ceramic

Abstract It aims on evaluate the effect of the test environment on static fatigue behavior of lithium disilicate-based (LD), and yttrium oxide-stabilized zirconia (YSZ) ceramics. Specimens of LD (IPS e.max CAD, Ivoclar Vivadent) and YSZ (IPS e.max ZirCAD MO, 3 mol% Y2O3, Ivoclar Vivadent) were randomly allocated into three groups: tested in air, inert (paraffin oil, Sigma Aldrich) or distilled water. The static fatigue test (n=15) was performed using a piston-on-three ball assembly, adapted from ISO 6872, as follows: starting load 100 N for LD and 300 N for YSZ; loading application time set to 1 hour for each loading step; step size of 50 N for LD and 100 N for YSZ, applied successively until fracture. Data from static fatigue strength (MPa) and time to fracture (hours) were recorded. Fractographic analysis was executed. Survival analysis corroborates absence of influence of environment on static fatigue outcomes (fatigue strength, time to fracture and survival rates) for YSZ. For LD, specimens tested in air presented statistically superior survival rate and static fatigue strength (p= 0.025). In regards of time to fracture, LD tested in air were superior than when tested in distilled water (p=0.019) or inert (p=0.017) environments. No statistical differences for Weibull modulus were observed. Failures started on the tensile stress surface. Thus, the test environment did not affect slow crack growth (SCG) mechanisms during static fatigue test of YSZ ceramics, but it plays a significant role for the static fatigue behavior of lithium disilicate-based glass ceramics, indicating a high susceptibility to SCG.

Resumo O presente estudo objetivou investigar a influência do ambiente de teste no comportamento a fadiga estática (resistência à fratura e tempo para falha) de cerâmicas à base de dissilicato de lítio (LD) e zircônia estabilizada com ítria (YSZ). Espécimes de LD (IPS e.max CAD, Ivoclar Vivadent) e YSZ (IPS e.max ZirCAD MO, 3mol% Y2O3, Ivoclar Vivadent) foram obtidos e alocados aleatoriamente em três grupos: testado em ar, em líquido inerte (óleo de parafina) ou em água destilada. O teste de fadiga estática (n= 15) foi realizado usando o teste pistão sobre três esferas, ISO 6872, da seguinte forma: carga inicial 100 N para LD e 300 N para YSZ; tempo de aplicação de carregamento definido para 1 hora para cada etapa de carregamento; tamanho do passo de 50 N para LD e 100 N para YSZ, aplicados sucessivamente até a fratura. Dados de resistência à fadiga estática (MPa) e tempo até a fratura (horas) foram registrados. A análise fractográfica foi executada. A análise de sobrevivência corrobora a ausência de influência do ambiente de teste nos resultados de fadiga estática (resistência à fadiga, tempo de fratura e taxas de sobrevivência) para a YSZ. Para LD, os corpos de prova testados em ar apresentaram taxa de sobrevivência e resistência à fadiga estática estatisticamente superiores (p= 0,025). Em relação ao tempo de fratura, os espécimes LD testados em ar foram superiores aos testados em água destilada (p= 0,019) ou em ambiente inerte (p= 0,017). Não foram observadas diferenças estatísticas para o módulo de Weibull. Todas as falhas começaram no lado onde se concentra a tensão de tração (lado de baixo) durante o teste. Com base nisso, observa-se que o ambiente de teste não afetou os mecanismos de crescimento lento de trinca durante o teste de fadiga estática da cerâmica YSZ, mas desempenha um papel significativo na resistência à fadiga estática da cerâmica de vidro à base de dissilicato de lítio, indicando alta susceptibilidade ao crescimento lento e subcrítico de trincas.

Polishing of ground y-tzp ceramic is mandatory for improving the mechanical behavior

Abstract It evaluated the effect of aging by Low Temperature Degradation (LTD), executed after post- processing surface treatments (polishing, heat treatment and glazing), on the surface characteristics (micromorphology and roughness) and on the structural stability (phase transformation and mechanical behavior-flexural strength and structural reliability) of a ground yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic. Discs of Y-TZP (VITA In-Ceram YZ) were manufactured (ISO:6872-2015; 15 mm in diameter and 1.2 ± 0.2 mm in thickness) and randomly assigned into 10 groups according two factors: "aging" in 2 levels (with or without) and "surface treatment" in 5 levels (Ctrl: as-sintered; Gr: grinding with coarse diamond bur; Gr + HT: grinding plus heat treatment; Gr + Pol: grinding plus polishing; Gr + Gl: grinding plus glazing). Roughness (n=30), biaxial flexural test (n=30), phase transformation (n=2), and surface topography (n=2) analyses were performed. Aging led to an intense increase in monoclinic (m) phase content for all the tested conditions, being the as-sintered samples (Ctrl= 65.6%) more susceptible to the t-m phase transformation. Despite of increasing the m-phase content, aging was not detrimental for characteristic strength (except to the grinding condition). There was no significant reduction in the Weibull modulus after surface treatments. Additionally, heat treatment and glazing after grinding led to a decrease in characteristic strength, while polishing presented the highest characteristic strength values. Thus, polishing is mandatory after grinding the Y-TZP ceramic, while performing glazing or heat-treatment alone after grinding lead to the worst mechanical performance.

Resumo Este estudo avaliou o efeito do envelhecimento através da degradação a baixas temperaturas (low temperaturare degradation - LTD) após a realização de tratamentos de superfície pós- sinterização (polimento, tratamento térmico e glaze) nas características superficiais (micromorfologia e rugosidade), e na estabilidade estrutural (transformação de fase e comportamento mecânico - resistência flexural e confiabilidade estrutural) de uma cerâmica de zircônia tetragonal policristalina estabilizada por ítria (Y-TZP) desgastada. Discos de cerâmica Y-TZP (VITA In-Ceram YZ) foram confeccionados (ISO:6872-2015; 15mm de diâmetro e 1,2 ± 0,2mm de espessura) e randomicamente divididos em 10 grupos de acordo com dois fatores: "envelhecimento" (com e sem) e "tratamento de superfície" (Ctrl - sem tratamento; Gr - desgaste com ponta diamantada grossa; Gr + HT - desgaste mais tratamento térmico; Gr + Pol - desgaste mais polimento; Gr + Gl - desgaste mais glazeamento). Foram realizadas as análises de rugosidade (n=30), flexão biaxial (n=30), transformação de fase (n=2) e topografia de superfície (n=2). O envelhecimento levou a um aumento intenso no conteúdo de fase monoclínica (m) em todas as condições testadas, sendo observada uma maior susceptibilidade de transformação de fase t-m nas amostras do grupo controle (Ctrl= 65.6%). Apesar de provocar elevada transformação de fase, o envelhecimento não apresentou efeitos negativos nos desfechos avaliados. Não houve redução significativa do módulo de Weibull após os tratamentos. Além disso, o tratamento térmico e o glaze após desgaste levaram a uma redução da resistência característica, enquanto que o grupo polimento apresentou o mais alto valor de resistência característica. O glaze e o tratamento térmico geraram o pior desempenho mecânico, portanto a realização do polimento após desgaste de uma cerâmica Y-TZP é obrigatória.

Effect of Grinding and Multi-Stimuli Aging on the Fatigue Strength of a Y-TZP Ceramic

Abstract This study aimed to investigate the effect of grinding and multi-stimuli aging on the fatigue strength, surface topography and the phase transformation of Y-TZP ceramic. Discs were manufactured according to ISO-6872:2008 for biaxial flexure testing (diameter: 15 mm; thickness: 1.2 mm) and randomly assigned considering two factors "grinding" and "aging": C- control (as-sintered); CA- control + aging; G- ground; GA- ground + aging. Grinding was carried out with coarse diamond burs under water-cooling. Aging protocols consisted of: autoclave (134°C, 2 bars pressure, 20 hours), followed by storage for 365 days (samples were kept untouched at room temperature), and by mechanical cycling (106 cycles by 20 Hz under a load of 50% from the biaxial flexure monotonic tests). Flexural fatigue strengths (20,000 cycles; 6 Hz) were determined under sinusoidal cyclic loading using staircase approach. Additionally, surface topography analysis by FE-SEM and phase transformation analysis by X-ray Diffractometry were performed. Dixon and Mood methodology was used to analyze the fatigue strength data. Grinding promotes alterations of topographical pattern, while aging apparently did not alter it. Grinding triggered t-m phase transformation without impacting the fatigue strength of the Y-TZP ceramic; and aging promoted an intense t-m transformation that resulted in a toughening mechanism leading to higher fatigue strength for as-sintered condition, and a tendency of increase for ground condition (C < CA; G = GA). It concludes that grinding and aging procedures did not affect deleteriously the fatigue strength of the evaluated Y-TZP ceramic, although, it promotes surface topography alterations, except to aging, and t-m phase transformation.

Resumo Este estudo objetivou investigar o efeito do desgaste e envelhecimento (estímulos combinados) na resistência à fadiga, topografia superficial e transformação de fase de uma cerâmica Y-TZP. Discos para teste de flexão biaxial foram confeccionados segundo as normas da ISO-6872:2008 (15 mm Ø; 1,2 mm espessura) e randomicamente distribuídos de acordo com os fatores "desgaste" e "envelhecimento": C- controle (sinterizado); CA- controle envelhecido; G- desgaste; GA- desgaste envelhecido. O desgaste foi feito com pontas diamantadas de granulação grossa sob irrigação com água. Os protocolos de envelhecimento consistiram em: autoclave (134°C, 2 bar de pressão, 20 horas), 365 dias armazenados em temperatura ambiente, e ciclagem mecânica (106 ciclos a 20 Hz em um intervalo de carga de até 50% da carga monotônica observada em testes estáticos). A resistência à fadiga foi determinada para 20.000 ciclos à 6 Hz sob carregamento sinusoidal através do método de escada. Adicionalmente, análises de topografia superficial em microscopia eletrônica de varredura e de transformação de fase por difração de raios-X foram executadas. A metodologia de Dixon e Mood foi usada para analisar os dados de resistência à fadiga. Foi observado que o desgaste promove uma alteração de padrão topográfico superficial; enquanto o envelhecimento aparentemente não demonstra influência. Em relação à transformação de fase e resistência à fadiga, o desgaste desencadeou um aumento de fase m sem impactar na resistência à fadiga da cerâmica Y-TZP; já o envelhecimento promoveu uma intensa transformação de fase, resultando no mecanismo de tenacificação, que gerou um aumento na resistência à fadiga para a condição sinterizada e uma tendência a aumento na condição desgaste (C < CA; G = GA). Os dados elucidam que o desgaste e o envelhecimento não impactaram negativamente na resistência à fadiga da cerâmica Y-TZP, apesar de promoverem alterações de topografia superficial e intensa transformação de fase de t-m respectivamente.

Effect of grinding and aging on subcritical crack growth of a Y-TZP ceramic

Abstract This study aimed to investigate slow crack growth (SCG) behavior of a zirconia ceramic after grinding and simulated aging with low-temperature degradation (LTD). Complementary analysis of hardness, surface topography, crystalline phase transformation, and roughness were also measured. Disc-shaped specimens (15 mm Ø × 1.2 mm thick, n = 42) of a full-contour Y-TZP ceramic (Zirlux FC, Amherst) were manufactured according to ISO:6872-2008, and then divided into: Ctrl - as-sintered condition; Ctrl LTD - as-sintered after aging in autoclave (134°C, 2 bar, 20 h); G - ground with coarse diamond bur (grit size 181 μm); G LTD - ground and aged. The SCG parameters were measured by a dynamic biaxial flexural test, which determines the tensile stress versus stress rate under four different rates: 100, 10, 1 and 0.1 MPa/s. LTD led to m-phase content increase, as well as grinding (m-phase content: Ctrl - 0%; G - 12.3%; G LTD - 59.9%; Ctrl LTD - 81%). Surface topography and roughness analyses showed that grinding created an irregular surface (increased roughness) and aging did not promote any relevant surface change. There was no statistical difference on surface hardness among different conditions. The control group presented the lowest strength values in all tested rates. Regarding SCG, ground conditions were less susceptible to SCG, delaying its occurrence. Aging (LTD) caused an increase in SCG susceptibility for the as-sintered condition (i.e. G < G LTD < Ctrl < Ctrl LTD).

Mechanical behavior of yttria-stabilized tetragonal zirconia polycrystal: Effects of different aging regimens

Abstract This study aimed to characterize and compare the effect of different aging regimens on surface characteristic (topography and roughness), structural stability (phase transformation) and mechanical performance (Weibull analysis) of a Y-TZP ceramic. Discs (15 × 1.2 mm; VITA In-Ceram YZ) were prepared according to ISO 6872-2015 for biaxial flexural strength testing and randomly assigned into five groups (n = 30): as-sintered, no aging treatment (CTRL); 20 h in autoclave at 134°C, 2 bar pressure (AUT); intermittent mechanical loading at 20 Hz/106 load pulses (MechLoad); AUT followed by MechLoad (AUT+MechLoad); and storage in distilled water at 37°C, for 1 year (STO). The following analyses were performed: roughness (n = 30), surface topography (n = 2), phase transformation (n = 2) and biaxial flexure strength (n = 30). Phase transformation (increase of m-phase content) was shown to be a spontaneous, unavoidable and time-dependent process, occurring even under ambient conditions (dry storage after 1 year = 6.0% increase), and is considerably accelerated in the presence of moisture (STO = 17.6%; AUT= 63.1%; and AUT+MechLoad = 59.9%). For roughness parameters, only Ra was affected by aging, and the highest values were observed for AUT+MechLoad (0.25 ± 0.07 µm). For Weibull analysis, structural reliability (Weibull moduli) and characteristic strength were not impaired after aging, and some aging conditions led to increased values (highest weibull moduli in AUT, and highest characteristic strength in STO). Phase transformation proves to be a time-dependent spontaneous mechanism that is accelerated in the presence of different stimuli. However, none of the aging regimens had a negative effect on the characteristic strength and structural reliability of Y-TZP ceramic.